CNC kitchen also tested this. https://www.cnckitchen.com/blog/brick-layers-make-3d-prints-stronger
You won't find this built into any slicer because some assholes patented it and are defending the patent.
this post was submitted on 07 Feb 2025
41 points (100.0% liked)
3DPrinting
19239 readers
7 users here now
3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.
The r/functionalprint community is now located at: or !functionalprint@fedia.io
There are CAD communities available at: !cad@lemmy.world or !freecad@lemmy.ml
Rules
-
No bigotry - including racism, sexism, ableism, homophobia, transphobia, or xenophobia. Code of Conduct.
-
Be respectful, especially when disagreeing. Everyone should feel welcome here.
-
No porn (NSFW prints are acceptable but must be marked NSFW)
-
No Ads / Spamming / Guerrilla Marketing
-
Do not create links to reddit
-
If you see an issue please flag it
-
No guns
-
No injury gore posts
If you need an easy way to host pictures, https://catbox.moe/ may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is ![]()
Moderation policy: Light, mostly invisible
founded 2 years ago
MODERATORS
They troll patented it. It was already patented, the patent expired, then these dildos patented it again as an "improved technique" and in their application they pointed to a bunch of patents that have nothing to do with the brick layer method.
TLDW;? Will watch it after work, but I'm curious now. 😁
Not as drastic as I had hoped, but it looks like around 5% better layer adhesion provided you increase the flow rate slightly to fit in the gaps. It essentially makes a print that's more solid in the walls.
I saw elsewhere someone doing prints with transparent filament and they were also getting optically better prints with this.
Also, there's a pull request on Orca... Not sure when it'll come out, but they're working on building it into the slicer.
It looks like this was testing in tension? I image most of the improvements would happen in shear. Since that's where you make the crack more tortuous. In tension the increase in contact is very slight.
he mentions only vertical offset but I don't see why it could not be done horizontal if the lines are stop/started at regular intervals. Im guessing it would not be stronger though than a continuous line.
It could, but I don't think there would be any benefit. The key thing this does is make walls a bit closer to the theoretical perfect solid structure.
ok yeah when he talked about it sorta fitting in between the cracks. so yeah it is closer to more solid. Thanks that actually wraps my head around why better.